Plastic Diaphragm valve corrosion performance application table
Chemicals | Density | Temperature | PVDF | UPVC | CPVC | PTFE | FPM | EPDM |
Aqua regia | 20 | A | C | C | A | C | B | |
40 | A | C | C | A | B | |||
60 | A | A | C | |||||
80 | A | A | ||||||
100 | B | A | ||||||
Arsenate | Saturation | 20 | A | A | A | A | A | A |
40 | A | B | B | A | A | A | ||
60 | A | C | B | A | A | B | ||
80 | A | C | A | B | B | |||
100 | B | A | B | |||||
Barium sulfate | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | A | A | |||
100 | A | A | A | |||||
Barium chloride | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | A | A | |||
100 | A | A | A | |||||
Barium hydroxide | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | A | A | |||
100 | A | A | A | B | ||||
Barium nitrate | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | A | A | |||
100 | A | A | A | B | ||||
Barium sulfate | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | A | A | |||
100 | A | A | ||||||
Barium sulfide | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | A | ||||
100 | A | A | A | |||||
Benzaldehyde benzaldehyde | 10 | 20 | A | A | A | C | C | |
40 | B | A | ||||||
60 | ||||||||
80 | ||||||||
100 | ||||||||
Benzene | Pure | 20 | A | C | C | A | B | × |
40 | B | × | × | A | B | |||
60 | B | A | B | |||||
80 | C | A | B | |||||
100 | × | A | ||||||
Bleach | 12 | 20 | A | A | A | A | A | B |
40 | A | A | A | A | ||||
60 | A | A | A | |||||
80 | A | A | ||||||
100 | A | |||||||
Borax | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | |||||
100 | A | A | ||||||
Boric acid | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | B | A | A | B | |||
100 | A | A | B |
Chemicals | Density | Temperature | PVDF | UPVC | CPVC | PTFE | FPM | EPDM |
Fluoboric acid | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | B | ||||
100 | A | A | ||||||
Brine | 20 | A | A | A | A | A | A | |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | A | B | |||
100 | A | A | B | |||||
Bromate | Pure | 20 | A | A | ||||
40 | A | A | ||||||
60 | A | A | ||||||
80 | A | A | ||||||
100 | A | |||||||
Brominevapor | 25 | 20 | A | B | A | A | × | |
40 | A | C | A | A | ||||
60 | A | A | A | |||||
80 | B | |||||||
100 | B | |||||||
Bromine | Saturation | 20 | A | B | C | A | A | × |
40 | A | C | A | A | ||||
60 | A | A | ||||||
80 | B | |||||||
100 | B | |||||||
Butadiene | Gas | 20 | A | A | A | A | A | × |
40 | A | A | A | A | A | |||
60 | A | A | A | A | ||||
80 | A | A | ||||||
100 | A | A | ||||||
Butyl Sulfuric Acid | Pure | 20 | A | A | ||||
40 | A | A | ||||||
60 | A | A | ||||||
80 | A | |||||||
100 | A | |||||||
Butyl benzyl alcohol | 20 | A | A | A | ||||
40 | A | A | A | |||||
60 | A | A | A | |||||
80 | A | A | A | |||||
100 | A | A | A | |||||
Butene | 20 | A | A | A | ||||
40 | A | A | A | |||||
60 | A | A | A | |||||
80 | A | A | B | |||||
100 | A | A | ||||||
Butyric acid | Pure | 20 | A | × | × | A | B | B |
40 | A | A | C | |||||
60 | A | A | × | |||||
80 | A | A | ||||||
100 | A | A | ||||||
Calcium carbonate | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | A | ||||
100 | A | B | A | A | ||||
Calcium chlorate | Saturation | 20 | A | A | A | A | A | A |
40 | A | A | A | A | A | A | ||
60 | A | A | A | A | A | A | ||
80 | A | A | A | |||||
100 | A | A | ||||||
Calcium hydroxide | Saturation | 120 | A | A | A | A | A | A |
140 | A | A | A | A | A | A | ||
160 | A | A | A | A | A | A | ||
180 | A | B | A | A | A | |||
200 | B | A | A |